S-11018.M

Thép cường độ cao S-11018.M

Type Basic
Industry Heavy Equipment|Offshore structures|Energy & Power Plants|Steel Fabric
JIS
EN ISO 18275-A - E62 2 Mn2NiMo B 1 2
KS
AWS A5.5/ASME SFA5.5 E11018-M
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.

    ② Preheat at 200~300℃(392~572℉).

    ③ Adopt back step method or strike the arc on a small steel plate prepared for this particular

    purpose because arc striking on the base metal is in danger of initiating cracking.

    ④ Pay attention not to exceed proper heat-input because excessive heat-input causes

    deterioration of impact values of all weld metal.
  • Purpose ① Low alloy high tensile steels
  • Attribute ① Iron powder and low hydrogen type electrode (high efficiency)

    ② Good crack resistance

    ③ Good X-ray performance

    ④ Good impact value at -50°C

S-9018.M

Thép cường độ cao S-9018.M

Type Basic
Industry Heavy Equipment|Offshore structures|Energy & Power Plants|Steel Fabric
JIS
EN ISO 18275-A - E50 4 Z1.5NiMo B 4 2
KS
AWS A5.5/ASME SFA5.5 E9018-M
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small plate prepared for this particular purpose because arc striking on base metal is in danger of initiating cracking.

    ③ Preheat at 80~100℃(172~212℉). The temperature to be applied varies in accordance with plate thickness and kind of steel.
  • Purpose ① Heavy steel fabrication

    ② Pressure vessels
  • Attribute ① Good crack resistance

    ② Good X-ray performance

    ③ Good impact value at -50°C

    ④ Iron powder and low hydrogen type electrode (high efficiency)

S-11016.G

Thép cường độ cao S-11016.G

Type Basic
Industry Heavy Equipment|Offshore structures|Energy & Power Plants|Steel Fabric
JIS
EN ISO 18275-A - E62 2 Mn2NiMo B 1 2
KS D7006 E8016
AWS A5.5/ASME SFA5.5 E11016-G
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose.

    ③ Preheat at 150~200℃(302~392℉). The temperature varies in accordance with plate thickness and kind of steel.
  • Purpose ① Heavy steel fabrication

    ② Pressure vessels

    ③ Power plant
  • Attribute ① Good crack resistance

    ② Good mechanical properties

S-10016.G

Thép cường độ cao S-10016.G

Type Basic
Industry Shipbuilding|Offshore Structures|Steel Fabrication
JIS Z3211 E6916-N4CM1 U
EN ISO 18275-A - E55 0 Z 1.5NiMo B 1 2
KS D7006 E7016
AWS A5.5/ASME SFA5.5 E10016-G
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose.

    ③ Preheat at 100~150℃(212~302℉). The temperature varies in accordance with plate thickness and kind of steel.
  • Purpose ① Heavy steel fabrication

    ② Pressure vessels

    ③ Power plant
  • Attribute ① Good crack resistance

    ② Good X-ray performance

    ③ Good mechanical properties.

S-9016.G

Thép cường độ cao S-9016.G

Type Basic
Industry Steel Fabrication
JIS Z3211 E5716
EN ISO 2560-A - E50 2 B 1 2
KS D7006 E5816
AWS A5.5/ASME SFA5.5 E9016-G
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose because arc striking on the base metal is in danger of initiating cracking.

    ③ Keep the arc as short as possible.

    ④ Preheat at 60~80℃(140~176℉) before use. The temperature to be applied varies in accordance with plate thickness and steel kind.

    ⑤ If each pass welds becomes thicker than acceptable level by high amperage of low speed ratio manipulation, the impact values and yield points will decrease.
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Offshore structure
  • Attribute ① Good bead appearance

    ② Good crack resistance

    ③ Good X-ray performance

    ④ Good mechanical properties

S-8018.G

Thép cường độ cao S-8018.G

Type Basic
Industry Heavy Equipment|Offshore structures|Energy & Power Plants|Steel Fabric
JIS Z3211 E5518
EN ISO 2560-A - E46 2 1Ni B 3 2
KS D7006 E5316
AWS A5.5/ASME SFA5.5 E8018-G
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small plate prepared for this particular purpose because arc striking on the base metal is in danger of initiating cracking.

    ③ Keep the arc as short as possible.
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Offshore structure
  • Attribute ① Good bead appearance

    ② Good crack resistance

    ③ Good X-ray performance

    ④ Good mechanical properties

    ⑤ Iron powder and low hydrogen type electrode (high efficiency)

S-8016.G

Thép cường độ cao S-8016.G

Type Basic
Industry Steel Fabrication
JIS Z3211 E5516
EN ISO 2560-A - E46 3 1Ni B 1 2
KS D7006 E5316
AWS A5.5/ASME SFA5.5 E8016-G
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400 ℃(662~752℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting.

    ③ Use wind screen against strong wind.
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Offshore structure
  • Attribute ① Good bead appearance

    ② Good crack resistance

    ③ Good X-ray performance

    ④ Good mechanical properties

S-7048.V

Thép cường độ cao S-7048.V

Type Basic
Industry Shipbuilding|Steel Fabrication
JIS Z3211 E4948
EN ISO 2560-A - E42 3 B 3 5
KS D7006 E5016
AWS A5.1/ASME SFA5.1 E7048
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 300~350℃(572~662℉) for 60 minutes before use.

    ② Remove rust, water, oil and paint from the surface to be welded.

    ③ Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting
  • Purpose ① Heavy steel fabrication

    ② Automotive

    ③ Machinery
  • Attribute ① Suitable for tack welding

    ② Good at vertical down

    ③ Good restriking

    ④ Good bead appearance

    ⑤ Easy to remove slag

S-7028.F

Thép cường độ cao S-7028.F

Type Basic
Industry Steel Fabrication
JIS Z3211 E4928
EN ISO 2560-A - E42 2 B 7 4
KS D7006 E5026
AWS A5.1/ASME SFA5.1 E7028
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 350~400℃(662~752℉) for 60 minutes before use.

    ② Remove rust, water and oil from the surface to be welded before welding.
  • Purpose ① Heavy steel fabrication
  • Attribute ① Heavy iron powder type electrode

    ② High deposition rate

    ③ Easy to remove slag

S-7018.G

Thép cường độ cao S-7018.G

Type Basic
Industry Shipbuilding|Offshore Structures|Steel Fabrication
JIS Z3211 E4918
EN ISO 2560-A - E42 3 B 1 2 H5
KS D7006 E5016
AWS A5.1/ASME SFA5.1 E7018
Catalog MSDS TTR
  • Caution .
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Pressure vessels
  • Attribute ① Suitable for butt and fillet welding of heavy structure

    ② Good crack resistance and X-ray performance

    ③ Good mechanical properties

    ④ Iron powder and low hydrogen type electrode (high efficiency)

S-7016.G

Thép cường độ cao S-7016.G

Type Basic
Industry Energy & Power Plants|Steel Fabrication
JIS Z3211 E4916
EN ISO 2560-A - E42 3 B 1 2
KS D7006 E5316
AWS A5.1/ASME SFA5.1 E7016
Catalog TTR
  • Caution ① Dry the electrodes at 300~350℃(572~662℉) for 60 minutes before use

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting

    ③ Use wind screen against strong wind
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Pressure vessels
  • Attribute ① Suitable for butt and fillet welding of heavy structure

    ② Good crack resistance and X-ray performance

    ③ Good mechanical properties.

S-7016.LF

Thép cường độ cao S-7016.LF

Type Basic
Industry Steel Fabrication
JIS Z3211 E4916
EN ISO 2560-A - E42 3 B 1 2
KS D7006 E5016
AWS A5.1/ASME SFA5.1 E7016
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 300~350℃(572~662℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting.

    ③ Keep the arc as short as possible. "
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Pressure vessels
  • Attribute ① Suitable for butt and fillet welding of heavy structure

    ② Good crack resistance and X-ray performance

    ③ Good mechanical properties

    ④ Low fume

S-7016.H

Thép cường độ cao S-7016.H

Type Basic
Industry Steel Fabrication|Energy & Power Plants|Shipbuilding
JIS Z3211 E4916
EN ISO 2560-A - E42 3 B 1 2
KS D7006 E5016
AWS A5.1/ASME SFA5.1 E7016
Catalog MSDS TTR
  • Caution ① Dry the electrodes at 300~350℃(572~662℉) for 60 minutes before use.

    ② Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose to prevent blow hole at the arc starting.

    ③ Use wind screen against strong wind.
  • Purpose ① Heavy steel fabrication

    ② Shipbuilding

    ③ Pressure vessels
  • Attribute ① Suitable for butt and fillet welding of heavy structure

    ② Good crack resistance and X-ray performance

    ③ Good mechanical properties
top